Filament ROSA3D PLA-Silk 1.75mm Navy Blue

Description

1.75 mm PLA-Silk filament for 3D printing by ROSA3D. 0.8 kg of filament is wound on the spool. The recommended printing temperature is in the range from 185°C to 225°C, and the bed temperature during printing in the range of 40°C - 60°C, however, when using adhesives, heating the bed is not necessary.

Rosa3D is a Polish manufacturer of filaments intended for both hobby and industrial printing. Thanks to many years of experience and modern machinery, the company is able to provide good quality and accuracy of the diameter and roundness of the filament. Filament PLA Starter from Rosa3D was designed for beginner users of 3D printers. The simplicity of PLA Starter printing will allow you to enjoy aesthetic prints, and over time will convince you to print more and more complex and demanding projects.

PLA-Silk is a durable and easy-to-use filament characterized by intense color and exceptional gloss. It is characterized by low shrinkage and no unpleasant odor. The prints are characterized by excellent layer adhesion and very good detail reproduction. The filament is made of a mixture of plastics based on the biodegradable PLA biopolymer. It was made only of ingredients approved for contact with food. PLA-Silk can be printed with the same settings as PLA Starter. There is no need to slow down the printing speed. The filament is shiny already on the spool, the gloss does not only arise during printing, so it allows quite a lot of freedom in choosing the temperature. Nevertheless, we always recommend that you print the temperature tower first.

Features

• Color: Navy Blue
• Diameter: 1.75 mm
• Diameter tolerance: +/- 0.05mm
• Oval tolerance: +0.02 mm
• Printing temperature: 185°C to 225°C
• Bed temperature: 40°C to 60°C (when using washers or other means to increase the adhesion heating of the table is not required)
• Density 1.24 g/cm3
• Odorless smell
• Elongation at tensile 6%
• Tensile strength (to break) 53 MPa
• Modulus of elasticity at tensile 3500 MPa
• Heat deformation temperature 55°C
• Net weight: 0.8 kg