Filament ROSA3D PLA Plus ProSpeed 1.75mm White

Description

1.75 mm PLA filament for 3D printing by ROSA3D. 1 kg of filament is wound on the spool. The recommended printing temperature is in the range of 190°C to 230°C, and the temperature of the bed during printing in the range of 50°C to 70°C, however, when using adhesives, heating the bed is not necessary.

Rosa3D is a Polish manufacturer of filaments intended for both hobby and industrial printing. Thanks to many years of experience and modern machinery, the company is able to provide good quality and accuracy of the diameter and roundness of the filament.

The PLA Plus ProSpeed ​​series is dedicated to the industry. It is perfect for continuous printing, taking many hours, where there is a need to print at high speed.

The PLA Plus ProSpeed ​​filament offers better mechanical and temperature resistance than PLA Starter. The impact strength measured by the Izod method is almost 1.5 times higher than that of standard ABS, and after crystallization - more than twice as high. The filament is made of biodegradable biopolymer and is an alternative to styrene-based materials. PLA Plus ProSpeed ​​provides excellent print quality, good adhesion to the print bed, less warping and no irritating smell. It was made of ingredients approved for contact with food.

Features

• Color: White
• Diameter: 1.75 mm
• Diameter tolerance: +/- 0.05mm
• Oval tolerance: +/- 0.02mm
• Printing temperature: 190°C to 230°C
• Bed temperature: 50°C to 70°C (when using washers or other means to increase the adhesion heating of the table is not required)
• Print speed: 60 to 80 mm/s
• Density 1.22 g / cm3
• Odor: odorless
• Tensile strength (to break) XY axis - 40 MPa; YX axis - 32 MPa; ZX axis - 24 MPa
• Modulus of elasticity in tension XY axis - 2865 MPa; YX axis - 2447 MPa; ZX axis - 2477 MPa
• Heat deformation temperature 75-85 ° C (after annealing)
• Impact strength according to the Izod method with the notch XY axis - 160 J / m; YX axis - 21 J / m; ZX axis - 109 J / m
• Net weight: 1 kg