Fiberlogy PLA Impact Black filament with a 1.75mm diameter and 1.00kg net weight, designed for FFF/FDM printing of functional parts, prototypes and components exposed to mechanical loads. The material combines PLA printability with increased impact resistance, 40MPa tensile strength and a heat deflection temperature of 75–85°C after annealing. Fiberlogy 3S-PLA.IMPACT-REFILL-BLACK-100-175

24h
Available
Available quantity: 3

Description

Fiberlogy PLA Impact Black 1.75mm 1.00kg filament is designed for FFF/FDM printing of functional prototypes, replacement parts, brackets, tools and other components requiring greater resistance to impact and cracking than standard PLA. The Black variant provides a black finish, while the material properties support both technical applications and parts requiring good reproduction of fine details.

Tensile strength reaches 40MPa, while tensile modulus is 2870MPa. Flexural strength reaches 73MPa, with a flexural modulus of 2410MPa. According to the TDS, notched Izod impact strength at 23°C is 160kJ/m. Mechanical properties marked for printed parts were measured on XY specimens with 100% infill after annealing at 110°C for 15min.

The recommended printing temperature is 220–245°C, while the bed temperature range is 50–70°C. An enclosed chamber is not required, allowing the material to be processed on typical FFF/FDM printers.

PLA Impact is suitable for applications requiring increased mechanical resistance without the more demanding printing conditions associated with some engineering materials. Typical applications include functional prototypes, brackets, working parts and components exposed to mechanical loads.

Example print made with Fiberlogy PLA Impact filament

Material density is 1.22g/cm³. Glass transition temperature is 55–60°C, while melting temperature is 165–180°C. After annealing, heat deflection temperature at 0.45MPa reaches 75–85°C. The 1.75mm filament is manufactured with a diameter tolerance of ±0.02mm and average roundness variation of ±0.01mm. The 1.00kg variant is supplied on the new spool system compatible with BambuLab AMS.

Features

Basic parameters

  • Brand: Fiberlogy
  • Series: PLA Impact
  • Color: Black
  • Material type: high-impact PLA
  • Printing technology: FFF/FDM
  • Filament diameter: 1.75mm
  • Diameter tolerance: ±0.02mm
  • Average roundness variation: ±0.01mm
  • Net weight: 1.00kg
  • Package type: spool
  • New spool system
  • Compatible with BambuLab AMS

Printing parameters

  • Printing temperature: 220–245°C
  • Bed temperature: 50–70°C
  • Enclosed chamber: not required

Mechanical properties

  • Density: 1.22g/cm³
  • Tensile strength: 40MPa (ASTM D638)
  • Tensile modulus: 2870MPa (ASTM D638)
  • Flexural strength: 73MPa (ASTM D790)
  • Flexural modulus: 2410MPa (ASTM D790)
  • Notched Izod impact strength at 23°C: 160kJ/m (ASTM D256)

Thermal properties

  • Heat deflection temperature at 0.45MPa after annealing: 75–85°C (ASTM E2092)
  • Glass transition temperature Tg: 55–60°C (ASTM D3418)
  • Melting temperature Tm: 165–180°C (ASTM D3418)
  • Specified test conditions: XY orientation, 100% infill, annealed at 110°C / 15min
1207403

Data sheet

Rodzaj filamentu
PLA Impact
Ilość filamentu
1 kg
Diameter
1,75 mm
Colour
Black
Type of packaging
Refill

Manufacturer

Responsible person

You might also like

Other products in the same category (16)